Impact of preheating on the mechanical performance of different MgO–C bricks - Low temperature range

This work complements an initial study regarding the mechanical behavior of MgO–C bricks at 1000 °C. In this case, two bricks bonded with phenolic resin, one of them containing aluminum, were treated at 600 °C and mechanically tested at RT and 600 °C. The thermal treatments attempt to simulate the in-service steelmaking ladle preheating process. At low temperatures, the binder pyrolysis is one of the main transformations and the Al melting neither its chemical reactions occur on a large scale yet. To evaluate the effects as the pyrolysis progresses, the soaking time at 600 °C was varied from 1 to 3 h. Although without significant chemical activity, the presence of Al affected the mechanical behavior of the tested bricks. The consolidation of the C–C network coming from the binder pyrolysis was identified as the main factor responsible for counterbalancing the material's degradation by microcracking. The heating combined with the low compressive pre-load applied on the tested specimens appears to close the microcracks and pores.     

Leucokinins: Multifunctional Neuropeptides and Hormones in Insects and Other Invertebrates

Leucokinins (LKs) constitute a neuropeptide family first discovered in a cockroach and later identified in numerous insects and several other invertebrates. The LK receptors are only distantly related to other known receptors. Among insects, there are many examples of species where genes encoding LKs and their receptors are absent. Furthermore, genomics has revealed that LK signaling is lacking in several of the invertebrate phyla and in vertebrates. In insects, the number and complexity of LK-expressing neurons vary, from the simple pattern in the Drosophila larva where the entire CNS has 20 neurons of 3 main types, to cockroaches with about 250 neurons of many different types. Common to all studied insects is the presence or 1–3 pairs of LK-expressing neurosecretory cells in each abdominal neuromere of the ventral nerve cord, that, at least in some insects, regulate secretion in Malpighian tubules. This review summarizes the diverse functional roles of LK signaling in insects, as well as other arthropods and mollusks. These functions include regulation of ion and water homeostasis, feeding, sleep–metabolism interactions, state-dependent memory formation, as well as modulation of gustatory sensitivity and nociception. Other functions are implied by the neuronal distribution of LK, but remain to be investigated.     

Dual pH‐ and thermal‐responsive nanocomposite hydrogels for controllable delivery of hydrophobic drug baicalein

Hydrogels have been widely used as mild biomaterials due to their bio‐affinity, high drug loading capability and controllable release profiles. However, hydrogel‐based carriers are greatly limited for the delivery of hydrophobic payloads due to the lack of hydrophobic binding sites. Herein, nano‐liposome micelles were embedded in semi‐interpenetrating poly[(N‐isopropylacrylamide)‐co‐chitosan] (PNIPAAm‐co‐CS) and poly[(N‐isopropylacrylamide)‐co‐(sodium alginate)] (PNIPAAm‐co‐SA) hydrogels which were responsive to both temperature and pH, thereby establishing tunable nanocomposite hydrogel delivery systems. Nano‐micelles formed via the self‐assembly of phospholipid could serve as the link between hydrophobic drug and hydrophilic hydrogel due to their special amphiphilic structure. The results of transmission and scanning electron microscopies and infrared spectroscopy showed that the porous hydrogels were successfully fabricated and the liposomes encapsulated with baicalein could be well contained in the network. In addition, the experimental results of response release in vitro revealed that the smart hydrogels showed different degree of sensitiveness under different pH and temperature stimuli. The results of the study demonstrate that combining PNIPAAm‐co‐SA and PNIPAAm‐co‐CS hydrogels with liposomes encapsulated with hydrophobic drugs is a feasible method for hydrophobic drug delivery and have potential application prospects in the medical field. © 2018 Society of Chemical Industry     

Mixture ratio modeling of dynamic systems

Any knowledge extraction relies (possibly implicitly) on a hypothesis about the modelled-data dependence. The extracted knowledge ultimately serves to a decision-making (DM). DM always faces uncertainty and this makes probabilistic modelling adequate. The inspected black-box modeling deals with “universal” approximators of the relevant probabilistic model. Finite mixtures with components in the exponential family are often exploited. Their attractiveness stems from their flexibility, the cluster interpretability of components and the existence of algorithms for processing high-dimensional data streams. They are even used in dynamic cases with mutually dependent data records while regression and auto-regression mixture components serve to the dependence modeling. These dynamic models, however, mostly assume data-independent component weights, that is, memoryless transitions between dynamic mixture components. Such mixtures are not universal approximators of dynamic probabilistic models. Formally, this follows from the fact that the set of finite probabilistic mixtures is not closed with respect to the conditioning, which is the key estimation and predictive operation. The paper overcomes this drawback by using ratios of finite mixtures as universally approximating dynamic parametric models. The paper motivates them, elaborates their approximate Bayesian recursive estimation and reveals their application potential.     

Improved rheological properties and stability of multiwalled carbon nanotubes/polymer in harsh environment

This work aims to improve the rheological properties and stability of multiwalled carbon nanotubes (MWCNTs)/acrylamide (AA) base skeleton polymer blends at harsh environment of high salinity-high temperature (HS-HT) or various pH. Different co/terpolymers have been accomplished to modify the structure of AA polymer by free-radical copolymerization of AA-based monomers. Anionic, cationic, and hydrophobic functional groups were used for the synthesis of polyelectrolyte, polyampholytic, and partially hydrophobic AA polymer types. The conversion, molecular weight, and poly dispersity of co/terpolymers have been evaluated by nuclear magnetic resonance (¹H-NMR), gel permeation chromatography, and differential scanning calorimetry analysis. The effects of sonication power, concentration of polymer, and concentration of MWCNTs were also investigated on rheological behavior of co/terpolymers. The results show that negative polyelectrolyte and polyampholytic polymers are the best candidates for the improvement of MWCNTs/polymer stability and viscosity at HS-HT and alkali environment, respectively. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47205.     

Invited review: Freedom from thirst—Do dairy cows and calves have sufficient access to drinking water?

The importance of drinking water for production and animal welfare is widely recognized, but surveys and animal welfare assessment schemes suggest that many dairy calves and dairy cows do not have sufficient access. Limit milk-fed calves drink more water than calves fed milk ad libitum, but ad libitum milk-fed calves also require access to drinking water, as milk does not meet the animal's requirement for water. At hot ambient temperatures and when calves are sick, access to water is especially important and should be provided at all times. Many young calves do not have access to water throughout 24 h, and whether healthy young calves require free access to water at all times, or from which age, is not clear and requires further study. Dairy cow free water intake (FWI) is largely determined by milk yield, and high-yielding dairy cows may drink up 100 L of water per day. Dry matter, crude protein, and salt content of feed, as well as ambient temperature, have considerable effects on dairy cow water intake. Deprivation of water affects meal patterning for the cow, as well as increased subsequent rate of drinking and compensatory water intake. Although dairy cow ad libitum water intake may exceed the water provision necessary to maintain production, offering water for ad libitum intake may be necessary to safe guard animal welfare. Cattle are suction drinkers that prefer to drink from large open water surfaces, and Holstein dairy cows can drink at a rate of up to 24 L/min. Research on the effect of design and placement of water troughs for indoor-housed dairy cows on their drinking behavior and water intake is limited. Access to a water source at pasture increases the time cows spend there, and access to shade reduces water requirements during periods of warm weather. In both indoor and pastured cattle, there is a lack of knowledge about the effect of stocking of water troughs on competition, drinking behavior, and intake in dairy cows. Studies on the effect of available water trough length and placement, and of the number of cows being able to drink from the same trough of a given dimension, are needed to evaluate current recommendations.     

Impact of high-intensity ultrasound on physical properties and degree of oxidation of lipase modified menhaden oil with caprylic acid and/or stearic acid

The purpose of this research was to determine the effect of high-intensity ultrasound (HIU) on physical properties, degree of oxidation, and oxidative stability of structured lipids (SLs). Caprylic acid (C) and stearic acid (S) were incorporated into menhaden oil using Lipozyme® 435 lipase to obtain five samples: (1) LC 20 (menhaden oil with 20% of C), (2) LC 30 (menhaden oil with 30% C), (3) LS 20 (menhaden oil with 20% S), (4) LS 30 (menhaden oil with 30% S), and (5) Blend C (menhaden oil with 16.24% C and 13.04% S). Samples were crystallized for 90 min at the following temperatures: (1) LC 20 at 15.5°C, (2) LC 30 at 17.5°C, (3) LS 20 at 24°C, (4) LS 30 at 30°C, and (5) Blend C at 18.0°C, and HIU was applied at the onset of crystallization. Physical properties, degree of oxidation, and oxidative stability were evaluated in sonicated and nonsonicated samples. All SLs had statistically higher G′ after sonication. Sonicated LS 30, LC 30, and Blend C had a higher melting enthalpy than the nonsonicated ones, while enthalpy values in sonicated LS 20 and LC 20 samples were not statistically different than the nonsonicated ones. No significant difference between sonicated and nonsonicated samples was observed in peroxide values (1.2 ± 0.1 meq/kg, p > 0.05) and in the oxidative stability index (6.3 ± 0.2 h, p > 0.05). These results showed that HIU was effective at changing physical properties without affecting the oxidation of the samples.     

Gelling behavior of MgAl2O4 slurries with a common dispersant

MgAl₂O₄ transparent ceramics were shaped by a commonly used polyacrylic acid (PAA), which acted as both dispersant and gelling agent. The spinel slurries were prepared by ball-milling MgAl₂O₄ powder, PAA, and water in an attrition mill. The gelling of slurries happened at room temperature in air atmosphere without any other organic additive. The gelling mechanism was the formation of chelates between Mg²⁺ and carboxyl groups (-COO⁻) of PAA. The frequency-based testing method was applied to investigate the gelling process of the as-prepared slurry. In addition, a novel in situ characterization method based on a modified indentation testing was invented to better understand the strengthening of the wet green body with time and to guide when demolding could be carried out. After sintering, transparent MgAl₂O₄ ceramics with high in-line transmittance were resulted.     

High temperature oxidation behavior of MoSi2–Al2O3 composite coating on TZM alloy

A novel MoSi₂–Al₂O₃ composite coating was prepared on Mo-based TZM alloy by slurry sintering method. The oxidation behavior of the coating was evaluated at 1600 °C in static air. Microstructure and phase composition of the as-prepared and oxidized coatings were characterized, and the antioxidant mechanism of the coating at high temperature was discussed. A three-layer structure was observed in the as-prepared coating, consisting of a ～2 μm thick Mo₅Si₃ diffusion layer, a ～65 μm thick MoSi₂ inner layer and a ～36 μm thick outer layer of mixture of MoSi₂ and Al₂O₃. After oxidation at 1600 °C for 5 h, all MoSi₂ phases were completely converted to intermediate silicide Mo₅Si₃ by solid-state diffusion, and the formed Mo₅Si₃ phase would be transformed into Mo₃Si phase with further extending the oxidation time. Furthermore, a dense oxide layer of SiO₂-mullite was formed on the specimen surface, which can effectively protect the material to further oxidation. The MoSi₂–Al₂O₃ coating could protect the substrate effectively at 1600 °C for 20 h without failure. The enhanced oxidation resistance of MoSi₂–Al₂O₃ coating is due to the formation of multi-layer structure containing a SiO₂-mullite composite oxide outer layer with high thermal stability and low oxygen permeability.     

Ablation behavior of (TiZrHfNbTa)C high-entropy ceramics with the addition of SiC secondary under an oxyacetylene flame

The ablation behavior of high-entropy ceramics (HECs) was investigated in this study using an oxyacetylene flame at 2000 °C. Spark plasma sintering was used to construct a dense HEC (TiZrHfNbTa)C with a 20 vol% of SiC addition (HEC-20SiC). The densification of HEC-20SiC can be improved to a certain extent by adding SiC particles, increasing the hardness of HEC-20SiC to up to 24.6 GPa, and the crack deflection observed through the addition of SiC particles were considered to be the strengthening and toughening mechanisms. After ablation, Hf₆Ta₂O₁₇, Ti_5.1Ta_4.9O₂₀, Nb₂Zr₆O₁₇, TaZr_2.75O₈, and SiO₂ can be detected on an ablated surface and HEC-20SiC possesses the minimum mass ablation rate (?1.9 mg s^?1) and line ablation rate (2.1 μm s^?1) among the comparative ceramics. On the one hand, the SiC phase forms gaseous CO, CO₂, and SiO as well as viscous SiO₂ during ablation and some part of the heat can be dissipated by the evaporation of gaseous CO, CO₂, and SiO; further, pore defects can be healed by viscous SiO₂, thus inhibiting the diffusion of reactive oxygen species. On the other hand, the HEC phase with a lattice-distortion caused by single-phase solid-solution can effectively inhibit the invasion of reactive oxygen species and the outward migration of metal atoms. The invasion rate of reactive oxygen is considered to be the main step during HEC-20SiC ablation, and it is believed that higher principal component HECs can improve ablation performance even further.